Resistivity of Nichrome

In: Science

Submitted By alekseikuryla
Words 1924
Pages 8
IB Higher Physics
Internal Assessment

Candidate Name: Aleksei Kuryla
Candidate Number:

Title: resistivity of nichrome

|D |DCP |CE |
| | | |

DATA COLLECTION AND PROCESSING

| |Criteria |( |Mark |Comments |
|Aspect 1 |Raw results only shown | | | |
| |Correct units | | | |
| |Uncertainties shown | | | |
| |Uncertainties justified | | | |
| |Uncertainties to 1 sig fig | | | |
| |Decimal places consistent with uncertainty | | | |
|Aspect 2 |Processed results shown in separate table | | | |
| |All necessary values shown | | | |
| |Correct units | |…...

Similar Documents

Resistance of a Wire

...In this experiment you will be making measurements of voltage and current for a piece of metal wire, together with the physical dimensions of the wire, from which you will calculate the resistivity of the metal. Theory The resistance R of a component in a circuit is given by the equation V = IR where V is the potential difference across the component and I is the current in the component. The resistance of a wire is given by the equation R = ρl / A where ρ is the resistivity of the metal from which the wire is made, l is the length of the wire and A is its cross-sectional area. Using the circuit below, you will make measurements of current and voltage for different lengths of wire. You will plot a graph of resistance against length and from this you will calculate the resistivity. A V flying lead zero end of the metre rule tape to hold wire into place resistance wire 70 © University of Cambridge International Examinations 2006 Teaching AS Physics Practical Skills Resistivity of a wire Student Worksheet Making measurements and observations Use the micrometer screw gauge to measure the diameter d of the resistance wire in several places along the length. Each time you take a measurement at a new place, rotate the wire slightly. 1 Tape the wire to the metre rule so it cannot slip and the markings of the rule are visible. 2 Connect the circuit shown in the diagram above. The flying lead should have......

Words: 802 - Pages: 4

Flame Colors

...of energy absorbed will account for the presence of a spectral line. The emission spectrum may be used to observe the presence of an element in both qualitative and quantitative way. Elements may often be identified by the color they expose to a flame. MATERIALS AND METHODS In determining the flame colors of different metals, first of all make sure that you have a clean flame test wire or nichrome wire. Then after it, the loop of the nichrome wire must be heated in flames hottest region until there was no visible of color. There should be no change in color of the flame if it's clean and if it is not clean, clean it by dipping into the concentrated HCL provided, then hold the loop in the Alcohol lamp. Repeat this cleaning until there is no more change in the color of the flame. Next objective is to do the flame tests. Dip the nichrome wire's loop into the reagent solution, then hold the nichrome wire's loop in the hottest part of the alcohol lamp flame. After doing it, observe and make a note of the color of the flame on your Flame Test Chart. Clean the nichrome wire, then test another known reagent solution. Keep going until you have recorded the color of all of the known reagent solutions. Check results and then observe carefully and compute smoothly to avoid any mistake. RESULTS AND DISCUSSIONS When a metal or metal salt is burned, the input of thermal energy raises the electrons in the metal atom to a higher energy state. These electrons cannot......

Words: 1072 - Pages: 5

Investigation of the Resistance of a Wire

...Background In this investigation I am going to investigate what affect the resistance of a wire. Electricity flows in metals. Metal wires are made of millions of tiny metal crystals. Each crystal’s atoms are arranged in a regular pattern. The metal is full of ‘free’ electrons that do not stick to any particular atom. They fill the space between atoms in a metal. When these electrons move they create an electric current. Conductors have resistance, but some are worse than others. The free electrons keep bumping into atoms. A wires resistance depends on four main factors which are: Resistivity The length of the wire Cross sectional area The temperature of the wire I am going to investigate how the length of the wire affects the resistance. I have done a preliminary experiment to help me decide the best way to do my investigation. The results should also help me make a prediction. Preliminary Investigation Below are my results from the preliminary experiment (see table 1). I have taken three readings each from the Volts and current to make sure it is as accurate as possible Table 1 From the results I can see that as the length of the wire increases, the resistance increases as well. Furthermore I have noticed that if you double the length of the wire, the resistance is roughly doubled. E.g. when the length of the wire is 20cm the resistance is 3.14 ohms, when the length of the wire is 40cm the resistance is 6.18 ohms which is roughly double 3.14 ohms....

Words: 1588 - Pages: 7

Doctor

...that the intrinsic concentration lli varies with T as (2-18) where EGO is the energy gap at OaK in electron volts, k is the Boltzman constant in eV JOK (Appendix A), and A o is a constant independent of T. The constants EGO, J.Ln, J.Lp, and many other important physical quantities for germanium and Sec. 2-5 TRANSPORT PHENOMENA IN SEMICONDUCTORS / 29 TABLE 2-J Properties of germanium and silicont Property Ge 32 72.6 5.32 16 4.4 X 10" 0.785 0.72 2.5 X 10" 45 3,800 1,800 99 47 Si 14 28.1 2.33 12 5.0 X 10" 1.21 1.1 1.5 X 10'· 230,000 1 , 300 500 34 13 Atomic number . Atomic weight . Density, g/cm' . Dielectric constant (relative) . Atoms/em' . EGo, eV, at OOK . E G , e V, at 300 o K . ni at 300 o K, cm-' . Intrinsic resistivity at 300 o K, Il-cm . ... "n, cm'/V-s at 300ooK . "., em' /V-s at 300 K . D n, cm'/s = "nV7· . D p, ~m'/s = "pVT . t G. L. Pearson and W. H. Brattain, History of Semiconductor Research, Proc. IRE, vol. 43, pp. 1794-1806, December, 1955. E. M. Conwell, Properties of Silicon and Germanium, Part II, Proc. IRE, vol. 46, no. 6, pp . 1281-1299, June, 1958. silicon are given in Table 2-1. Note that germanium has of the order of 10 22 atoms/ cm 3, whereas at room temperature (300 0 K), ni ~ 10 13/ cm 3. Hence only 1 atom in about 10 9 contributes a free electron (and also a hole) to the crystal because of broken covalent bonds. For silicon this ratio is even smaller, about 1 atom in 10 12 The Energy Gop The forbidden region......

Words: 63477 - Pages: 254

Resistance and Resistivity

...[Your First Name Your Last Name] [Teacher’s Name] [Class Name/Period] [Date (January 26, 2015)] Resistance and Resistivity Resistance is the property of a substance which makes it oppose the flow of an electric current through it. Generally, metals acids and liquid salts and salt solutions are very good conductors of electricity. Metals with higher numbers of delocalized electrons have higher conductivities than those with fewer delocalized electrons. For example, aluminium is more conductive than copper which is also more conductive than copper. When an electric current is applied to a conductor, the delocalized electrons assume a directed motion depending on the polarity of the potential difference. As the electrons move, they collide and bombard with atoms and molecules of the conducting material, thereby creating heat (T. B. Theraja). Materials which offer higher hindrance to the flow of electrons on application of a potential difference are called poor conductors of electricity. Examples of poor conductors are: Polyvinyl chloride (PVC), dry wood, rubber, glass and mica. Insulators are used in the coating of conductors to prevent electrical shocks .Resistance is measured in ohms denoted Ω. Depending on the degree of resistances other commonly used units are; mega-ohms (M Ω), kilo-ohms (k Ω), mill-ohms (m Ω) and micro-ohms (μ Ω) (T. B. Theraja). Resistance of a material is derived from the factors affecting it. According to the laws of resistance, resistance is......

Words: 370 - Pages: 2

Investigating the Resistivity of a Wire

...thick wires have low resistance. Due to Ohm’s law which stated that the resistance of a wire id directly proportional to its length and inversely proportional to its thickness. Theory: The theory of this experiment is that the resistance R in the circuit of a component is given by this equatio n: V=IR Where as: * V is the potential difference across the component. (Volts) * I is the current in the component. (Ampers) * R is the resistance. (Ohms) The main factors that affect the resistance are the thickness of the wire, length of the wire and the temperature of the conductor and those factors also affect the current and voltage. The equation that gives the resistance of a wire is this equation: R=pLA Where as: * p is the resistivity (ohms) * L is the length (meters) * A is the cross-sectional area (meters2) Circuit Diagram: Recorded Data: * Table One (Thin Wire) | | | | | | | | | | Thin wire | | | | Wire Dia | length | V.res | V.wire | I | R |  | (mm) | (mm) | (V) | (V) | (A) |  | (m) |   |   |   |   | | |   |   |   |   |   | | |   |   |   |   |   | | |   | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | |   |   |   |   | | |   | | | | | | | | | | | | | (av) |   | * Table Two (Thick wire) | | | Thick wire | | | | Wire Dia | length |......

Words: 589 - Pages: 3

Ensc1002 Disassembly Project

...temperature-sensitive alloy which holds a spring contact mechanism normally closed. When the surrounding temperature gets too high, the alloy melts and allows the spring contact mechanism to break the circuit. Unlike electrical fuses or circuit breakers, thermal fuses only react to excessive temperature, not excessive current, unless the excessive current is sufficient to cause the thermal fuse itself to heat up to the trigger temperature. Important properties and why: The fuse element is made of zinc, copper, silver, aluminum, or alloys to provide stable and predictable characteristics. The metal strip or wire melts at a lower temperature than the wire and other components in the rest of the circuit. Fuse elements may be supported by steel or nichrome wires, so that no strain is placed on the element, but a spring may be included to increase the speed of parting of the element fragments. The fuse element may be surrounded by air, or by materials intended to speed the quenching of the arc. The material that the part is made from: A fuse consists of a metal strip or wire fuse element, of small cross-section compared to the circuit conductors, mounted between a pair of electrical terminals, and (usually) enclosed by a non-combustible housing. The fuse is arranged in series to carry all the current passing through the protected circuit. One mechanism is a small melt able pellet that holds down a spring. When the pellet melts, the spring is released, separating the contacts......

Words: 867 - Pages: 4

Bomb Calorimeter

...the two samples. With the combustion reaction that is happening with in the bomb, the data collected can be used to determine the potential maximum heat released by a fuel. A test sample of a known mass is combusted under standard conditions while the volume remains constant within pure oxygen atmosphere. Experimental: In this experiment each sample was weighed with the analytical scale, which was no more than 1.000g because the more sample used then the risk of the bomb being actually a “bomb”. Once that is weighed out, it was placed in the fuel capsule where the nichrome wire was then placed carefully where it was touching the sample. This part was very important because the wire must touch the sample but should not touch the fuel capsule because it will not ignite and burn the sample. The temperature was recorded with the electrical thermometer and when the combustion was done the left over nichrome wire was the weighed. After all of the temperatures are recorded for all samples the heat of capacity of the calorimeter was calculated. Data Analysis and Results: Table: 1 Raw Data | Benzoic Acid |   | TBDMB |   | CDDT |   | Temperature (°C) | Time (Seconds) | Temperature (°C) | Time (Seconds) | Temperature (°C) | Time (Seconds) | 21.77 | 0 | 19.85 | 0 | 19.84 | 0 | 21.77 | 15 | 19.86 | 15 | 19.84 | 15 | 21.77 | 30 | 19.86 | 30 | 19.84 | 30 | 21.77 | 45 | 19.86 | 45 | 19.84 | 45 | 21.77 | 60 | 19.87 | 60 | 19.84 | 60 | 21.77 | 75 | 19.87 | 75 |......

Words: 1253 - Pages: 6

Cation and Anion

...KI(aq) = AgI(s) + KNO3(aq) | | | | | Cation are positively charged ion, this means that it would be attracted to the cathode in electrolysis. A Cation will form when an element or atom lose one or more electron. Electrons are actually negatively charged particles for this reason when element loses an electron, it becomes less negative and more positive. Example of Cation are; hydrogen, barium, sodium, potassium, sliver, ammonium, calcium, iron, copper, lead, and aluminium. A flame test is a most test use to identity most of the Cation like iron and calcium. A Bunsen and burner and a nichrome wired looped is used for a flame test. The nichrome wire should be cleaned in hydrochloric acid concentration, to sure there is no contaminating flame colours. You dip the nichrome wired loop in the calcium or iron powder, then put it through the blue flame in the Bunsen burner and the nichrome wired loop should show colour change. For like calcium the colour will show an orange red. The colours in the flame test are due to the stimulation to a higher electronic energy levels. The light will emit as the electron return to a lower and stable electronic energy level. Aluminium, magnesium, iron and zinc do not produce a useful identifying flame colours. We can test for cations by adding sodium hydroxide solution and noting the colour of the precipitate. For the sodium hydroxide test if the Precipitate turns white like for aluminium and calcium, you need to add more sodium......

Words: 801 - Pages: 4

Che 350 Problem Set 3

...proposed. Is the proposed stead-state operation feasible? b. In the event of a loss of coolant, the heat transfer coefficient h would decrease drastically. Explore the effects of energy generation rate and heat transfer coefficient on the temperatures at the center of the fuel rod and at the fuel rod-cladding interface. Plot these temperatures as functions of volumetric energy generation rate in the fuel rod (over the range 100-1000 MWm-3) for different values of h (over the range 1-10 MWm-2K-1) in order to suggest an envelope of acceptable operating conditions. 2. Consider an electric space heater made of coiled Nichrome wire of 1 mm diameter, with cross flow of 50˚C air over the wire to establish a convective heat transfer coefficient of 250 Wm-2K-1. The housing that encloses the coiled wire is at Tsur = 50˚C. The Nichrome wire has electrical resistivity of ρe = 10 -6 Ωm, thermal conductivity of k = 25 Wm-1K-1, and surface emissivity of ε = 0.20. a. Assuming negligible temperature variations within the wire, estimate the maximum allowable electric current to avoid wire temperatures greater than 1200˚C. b. Assess the validity of the assumption of uniform wire temperature in part (a) by computing the centerline temperature corresponding to the maximum rate of heat generation. c. (Extra credit) What is the corresponding length of wire that may be used in the heater for a maximum available voltage of 110V? What is the power rating of the heater? 3.......

Words: 498 - Pages: 2

Che 350 Problem Set 3

...proposed. Is the proposed stead-state operation feasible? b. In the event of a loss of coolant, the heat transfer coefficient h would decrease drastically. Explore the effects of energy generation rate and heat transfer coefficient on the temperatures at the center of the fuel rod and at the fuel rod-cladding interface. Plot these temperatures as functions of volumetric energy generation rate in the fuel rod (over the range 100-1000 MWm-3) for different values of h (over the range 1-10 MWm-2K-1) in order to suggest an envelope of acceptable operating conditions. 2. Consider an electric space heater made of coiled Nichrome wire of 1 mm diameter, with cross flow of 50˚C air over the wire to establish a convective heat transfer coefficient of 250 Wm-2K-1. The housing that encloses the coiled wire is at Tsur = 50˚C. The Nichrome wire has electrical resistivity of ρe = 10 -6 Ωm, thermal conductivity of k = 25 Wm-1K-1, and surface emissivity of ε = 0.20. a. Assuming negligible temperature variations within the wire, estimate the maximum allowable electric current to avoid wire temperatures greater than 1200˚C. b. Assess the validity of the assumption of uniform wire temperature in part (a) by computing the centerline temperature corresponding to the maximum rate of heat generation. c. (Extra credit) What is the corresponding length of wire that may be used in the heater for a maximum available voltage of 110V? What is the power rating of the heater? 3.......

Words: 498 - Pages: 2

Batteries, Resistance and Current

...depends on its length, cross-sectional area, and the resistivity (the Greek letter rho), a number that depends on the material. The resistivity and conductivity are inversely related. Good conductors have low resistivity, while poor conductors (insulators) have resistivity’s that can be 20 orders of magnitude larger. Resistance also depends on temperature, usually increasing as the temperature increases. For reasonably small changes in temperature, the change in resistivity, and therefore the change in resistance, is proportional to the temperature change. Prelab: 1. Batteries are made by the difference in the electronegativity of different metals. Electrons can flow spontaneously between metals that give off electrons easier to metals that are less likely to give off electrons. There is a substance between these metals that allow charge to flow (salt bridge) so net charge doesn’t build up and “turn off” the battery. Draw a diagram (use your text) of an alkaline battery showing the + terminal, - terminal (and the type of metals used), the direction of current (+) flow and what’s inside. 2. What is the resistivity (ρ) of a resistor? What characteristics of a resistor affect the resistivity? Write a formula for this relationship, label each variable and indicate the units used to measure each. Would resistivity be constant for a specific resistor? 3. What is the difference between resistivity (ρ) and resistance (R)? What are the units of......

Words: 749 - Pages: 3

Che 350 Problem Set 3

...proposed. Is the proposed stead-state operation feasible? b. In the event of a loss of coolant, the heat transfer coefficient h would decrease drastically. Explore the effects of energy generation rate and heat transfer coefficient on the temperatures at the center of the fuel rod and at the fuel rod-cladding interface. Plot these temperatures as functions of volumetric energy generation rate in the fuel rod (over the range 100-1000 MWm-3) for different values of h (over the range 1-10 MWm-2K-1) in order to suggest an envelope of acceptable operating conditions. 2. Consider an electric space heater made of coiled Nichrome wire of 1 mm diameter, with cross flow of 50˚C air over the wire to establish a convective heat transfer coefficient of 250 Wm-2K-1. The housing that encloses the coiled wire is at Tsur = 50˚C. The Nichrome wire has electrical resistivity of ρe = 10 -6 Ωm, thermal conductivity of k = 25 Wm-1K-1, and surface emissivity of ε = 0.20. a. Assuming negligible temperature variations within the wire, estimate the maximum allowable electric current to avoid wire temperatures greater than 1200˚C. b. Assess the validity of the assumption of uniform wire temperature in part (a) by computing the centerline temperature corresponding to the maximum rate of heat generation. c. (Extra credit) What is the corresponding length of wire that may be used in the heater for a maximum available voltage of 110V? What is the power rating of the heater? 3.......

Words: 498 - Pages: 2

Assignment on Engineering Materials (Glass)

...going from the crystalline to the liquid state is due to the increased scattering of conduction electrons as a result of the increased amplitude of atomic vibration. Such theories of localization have been applied to transport in metallic glasses, where the mean free path of the electrons is very small (on the order of the interatomic spacing). Thus, if the electrical conductivity is low, the mean free path of the electrons is very short. The electrons will only be sensitive to the short-range order in the glass since they do not get a chance to scatter from atoms spaced at large distances. Since the short-range order is similar in glasses and crystals, the electronic energies should be similar in these two states. For alloys with lower resistivity and longer electronic mean free paths, the electrons could begin to sense that there is disorder in the glass, and this would raise their energies and destabilize the glass with respect to crystallization. Thus, the glass formation tendencies of certain alloys may therefore be due in part to the fact that the electron mean free paths are very short, so that only the short-range order is ever important for the energy of the electrons. Different types of Glass Borophosphosilicate glass Borophosphosilicate glass, commonly known as BPSG, is a type of silicate glass that includes additives of both boron and phosphorus. Silicate glasses such as PSG and borophosphosilicate glass are commonly used in semiconductor device......

Words: 6654 - Pages: 27

Alloy

...ship propellers and submerged bearings. It is also widely used for cast bronze sculpture. Many common bronze alloys have the unusual and very desirable property of expanding slightly just before they set, thus filling in the finest details of a mold. Bronze parts are tough and typically used for bearings, clips, connectors and springs. 5.NICHROME Composition: (Nickel & Chromium) Properties: High electrical resistivity & Resistance to oxidation. Applications: Nichrome is widely used in electric heating elements, such as in hair dryers, electric ovens, soldering iron, toasters, and even electronic cigarettes. Typically, Nichrome is wound in coils to a certain electrical resistance, and current is passed through to produce heat. Nichrome is used in the explosives and fireworks industry as a bridgewire in electric ignition systems, such as electric matches and model rocket igniters.Industrial and hobby hot wire foam cutters use nichrome wire. Nichrome wire is commonly used in ceramics as an internal support structure to help some elements of clay sculptures hold their shape while they are still soft. Nichrome wire is used because of its ability to withstand the high temperatures that occur when clay work is fired in a kiln.Nichrome wire can be used as an alternative to platinum wire for flame testing by colouring the non-luminous part of a flame to detect cations such as sodium, potassium, copper, calcium etc.The alloy tends to be expensive due to its......

Words: 1286 - Pages: 6

spider-man: into the spider-verse movie2k | Gru 3: Mi Villano Favorito | Zack és Cody a fedélzeten